17-4PH / SUS630 Neoksidebla ŝtalo
| DIN | ASTM | AISI | UNS | JIS | Alia |
| 1.4542 | |||||
| X5CrNiCuNb16-4 | Klaso 630 | 630 | S17400 | SUS 630 | 17-4PH |
| AMS 5643 | |||||
| AMS 5622 | |||||
| Z6CNU17-04 | |||||
| 10705GU-GV |
Kemia Komponado (%)
| C | Si | Mn | P | S | Cr | Ni | Mo | Alia |
|---|---|---|---|---|---|---|---|---|
| ≤ 0,07 | ≤ 1.00 | ≤ 1.00 | ≤ 0,040 | ≤ 0,030 | 15,0 ～ 17,0 | 3.00 ～ 5.00 | - | Cu 3.00 ～ 5.00 Nb + Ta 0,15 ～ 0,45 |
Mekanikaj Ecoj
| Kondiĉo de varma traktado | Streĉita Rm (MPa) | Rendimento Rp0.2 (MPa) | Plilongigo A (%) | Redukto en kruco sekcio pri frakturo Z (%) | Efiko AKV / AKU (J) | Brinell Malmoleco (HBW) |
|---|---|---|---|---|---|---|
| Kalcinita | ≤ 1034 | ≤ 650 | 6.0 ～ 15.0 | 30,0 ～ 60,0 | - | ≤ 363 |
| H900 | ≥ 1380 | ≥ 1275 | ≥ 14,0 | ≥ 50,0 | ≥ 20 | ≤ 420 |
| H925 | ≥ 1310 | ≥ 1200 | ≥ 14,0 | ≥ 54,0 | ≥ 34 | ≤ 409 |
| H1025 | ≥ 1170 | ≥ 1140 | ≥ 15,0 | ≥ 56,0 | ≥ 47 | ≤ 352 |
| H1075 | ≥ 1140 | ≥ 1035 | ≥ 16,0 | ≥ 58,0 | ≥ 61 | ≤ 341 |
| H1100 | ≥ 1035 | ≥ 930 | ≥ 17,0 | ≥ 58,0 | ≥ 61 | ≤ 332 |
| H1150 | ≥ 1000 | ≥ 860 | ≥ 19,0 | ≥ 60,0 | ≥ 68 | ≤ 311 |
| H1150 + H1150 | ≥ 965 | ≥ 760 | ≥ 20,0 | ≥ 60,0 | ≥ 108 | ≤ 302 |
| H1150M | ≥ 860 | ≥ 585 | ≥ 22,0 | ≥ 68,0 | ≥ 135 | ≤ 277 |
Formoj kaj Formoj:
Ronda stango (Diametro): 5,5 mm ĝis 700 mm
Drata stango (Diametro): 0.10 ~ 16mm
Kvadrata stango / plata stango: 5mm ĝis 550mm
Ŝtala strio per malvarma rulado: T0.1 - 3mm X W5 - 650mm XL (aŭ en volvaĵo)
Forĝita ringo: OD200 ~ 1500mm X ID150 ~ 1250mm X H20 ~ 1250mm
Peza / meza plato per varma rulado: T50 - 200mm X W80- 1200mm X L1000-3000mm
Forĝanta peco: paŝitaj ŝaftoj kun flankoj / diskoj / tuboj / limakoj / ringbulkoj / kuboj / aliaj malsamaj formoj bazitaj sur OEM.
Longo: Fiksa longo aŭ hazarda longo aŭ surbaze de la speciala postulo de la kliento.